合金鋼襯板
丁寶勤 13906276368(技術)
電話:0513-88400999 傳真:0513-88400998 郵箱:jszk@vip.163.com
 
合金鋼襯板主要用于水泥廠、選礦、火電廠以及立磨、自磨機等,合金鋼襯板在使用過程中耐磨性好,不變形,不破碎,可以提高磨機生產力,減少磨機停機時間,其使用壽命是普通高錳鋼的2-4倍。
| 序號 | 牌號 | 化學成份Chemical Compostion(%) | ||||||||
| C | Si | Mn | Cr | Mo | Ni | Cu | S | P | ||
| 1 | ZG30Gr5MoMnRe | 0.25-0.35 | 0.3-1.0 | 0.3-1.0 | 4.5-5.5 | 0.7-1.0 | 
 | 
 | ≤0.045 | ≤0.0045 | 
| 2 | ZG40Gr5MoMnRe | 0.35-0.45 | 0.3-1.0 | 0.3-1.0 | 4.5-5.5 | 0.7-1.0 | 
 | 
 | ≤0.045 | ≤0.045 | 
| 3 | ZG45Cr3NiMoMnRe | 0.40-0.50 | 0.3-0.8 | 0.6-1.2 | 2.0-3.2 | 0.3-0.5 | 0.5-1.0 | 
 | ≤0.04 | ≤0.04 | 
| 4 | ZG90Cr6MoMn | 0.85-0.95 | 0.4-0.8 | 0.3-0.8 | 5-8 | 0.2-0.4 | 
 | 
 | ≤0.04 | ≤0.04 | 
| 5 | ZGMn13 | 1.1-1.4 | 0.3-1.0 | 11-14 | 
 | 
 | 
 | 
 | ≤0.06 | ≤0.09 | 
| 6 | ZGMn13Cr2 | 1.1-1.4 | 0.3-1.0 | 11-14 | 1.5-2.5 | 0-0.5 | 
 | 
 | ≤0.06 | ≤0.08 | 
| 7 | ZGMn17Cr2 | 1.1-1.4 | 0.3-1.0 | 16-19 | 10-2.0 | 
 | Ti0.2-0.4 | 
 | ≤0.06 | ≤0.08 | 
| 8 | ZG20Cr26Ni5 | ≤0.20 | ≤2.0 | ≤2.0 | 22-26 | ≤0.50 | 4-6 | 
 | ≤0.04 | ≤0.04 | 
| 9 | ZG35Cr26Ni12 | 0.2-0.5 | ≤2.0 | ≤2.0 | 22-26 | ≤0.50 | 11-14 | 
 | ≤0.04 | ≤0.04 | 
| 10 | ZG40Cr26Ni20 | 0.35-0.45 | ≤2.0 | ≤2.0 | 23-27 | ≤0.50 | 19-22 | 
 | ≤0.04 | ≤0.04 | 
| 11 | KmTBCr15Mo2 | 2-2.8 | ≤1.0 | 0.5-1.0 | 12-18 | 0.5-2.5 | 0-1.0 | 0-1.2 | ≤0.06 | ≤0.10 | 
| 12 | KmTBCr20Mo2 | 2-3.0 | ≤1.0 | 0.5-1.0 | 18-22 | 1.5-2.5 | 0-1.5 | 0.8-1.2 | ≤0.06 | ≤0.10 | 
| 13 | KmTBCr26 | 2-3.0 | ≤1.0 | 0.5-1.0 | 22-28 | 0-1.0 | 0-1.5 | 0-2.0 | ≤0.06 | ≤0.10 | 
| 序號 | 牌號 | 機械性能 | 金相組織 | ||
| Ak/cm2 | HRC | abMpa | |||
| 1 | ZG30Gr5MoMnRe | ≥25 | ≥45 | 
 | M+B+C | 
| 2 | ZG40Gr5MoMnRe | ≥20 | ≥48 | 
 | M+B+C | 
| 3 | ZG45Cr3NiMoMnRe | ≥20 | ≥50 | 
 | M+C | 
| 4 | ZG90Cr6MoMn | ≥7 | ≥50 | 
 | M+C | 
| 5 | ZGMn13 | ≥147 | HB≤229 | 637 | A+C | 
| 6 | ZGMn13Cr2 | ≥80 | 
 | 
 | A+C | 
| 7 | ZGMn17Cr2 | ≥50 | 
 | 
 | A+C | 
| 8 | ZG20Cr26Ni5 | 
 | 
 | 590 | A+F | 
| 9 | ZG35Cr26Ni12 | 
 | 
 | 490 | A+F | 
| 10 | ZG40Cr26Ni20 | 
 | 
 | 440 | A+F | 
| 11 | KmTBCr15Mo2 | 
 | ≥53 | 
 | M+A+C | 
| 12 | KmTBCr20Mo2 | ≥3 | ≥58 | 
 | M+A+C | 
| 13 | KmTBCr26 | 
 | ≥52 | 
 | M+A+C | 